Pembuatan Keramik Berpori Sebagai Filter Gas Buang Dengan Aditif Karbon Aktif

Abstract

A research has done its about to fabricatied the porous ceramics aplicated as exaust gas filter with active carbon as aditif and furnace at 1100º C. The values shown there,s a significant corresponding between active carbon with the absorbstion. The rute materials for making ceramics are caolin, clay, feldspar, and quartzs, they all came from native materials, and its used slip casting method, then burned in temperature 1100º C .The porous ceramic,s characteristic are burned shrinking 1,96% - 3,59%, porosity 35,54% - 63,30%, density 1,36 gr/ cm3 – 0,70 gr/cm3, hardness 140 kgf/mm2 – 86 kgf/mm2, strength pressure 11,48 – 0,88 x 105 Pa, and the absorbtion of CO is 14% - 27,65%, CO2 7,85% -26,09%, HC 0,31% - 15,11%

Telah dilakukan penelitian tentang pembuatan keramik berpori sebagai filter gas buang kendaraan bermotor dengan aditif karbon aktif, dan pembakaran pada suhu 1100º C. Hasil yang diperoleh menunjukkan bahwa terdapat korelasi yang signifikan antara pertambahan karbon aktif dengan daya absorbsi keramik berpori.Keramik dibuat dengan bahan dasar kaolin, clay, feldspar, dan kuarsa yang semuanya dari daerah setempat, keramik dibuat dengan metode slip casting, dan pembakaran pada suhu 1100º C. Keramik berpori yang terbentuk adalah keramik berpori dengan ukuran susut bakar sebesar1,96% s/d 3,59%, porositas antara 35,54% s/d 63,30%, densitas 1,36 gr/cm3 s/d 0,70 gr/cm3, kekerasan 140 kgf/mm2 s/d 86 kgf/mm2, kekuatan tekan 11,48 x 105 s/d 0,88 x 105 Pa, serta dapat mengabsorbsi CO sebesar 14% s/d 27,65%, CO2 sebesar 7,85% s/d 26,09%,dan HC 0,31% s/d 15,11%.