Pemanfaatan Limbah Padat Pulp Dregs Sebagai Pengisi Batako Dengan Perekat Tepung Tapioka

Abstract

Batako and it’s characteristics had been investigate with the used of pulp solid waste dregs as filler and tapioca as adhesiveness. This research has been done by mixing method by using mixer. The aim is to have dregs as batako filler and the tapioca to get more value.The sample test was made into cube ( 5 cm x 5 cm x 5 cm ) and beam (length 12 cm, wide 3 cm and thick 3 cm) and ageing time 28 days.The parameter test are compressive strength , flexural strength , impact strength , density and water absorption. From the result indicates compressive strength and water absorption with the best composition varation is 60% dregs with cement and sand are constant.At those composition has the following material characteristic : Compressive strength = 8 MPa, Flexural strength = 0,14 MPa, Impact strength = 0,52 MPa, density = 1710 kg/m3 and water absorption = 4,98%.

Telah dilakukan penelitian tentang pembuatan dan karakterisrik batako dengan pemanfaatan limbah padat pulp dregs sebagai pengisi serta tapioka sebagai perekat. Penelitian ini dilakukan dengan metode pengadukan dengan menggunakan mixer yang bertujuan untuk memanfaatkan dregs sebagai pengisi dan tapioka untuk mendapatkan nilai lebih .Sampel yang dibuat berbentuk kubus dengan ukuran 5 cm x 5 cm x 5 cm dan berbentuk balok dengan panjang 12 cm, lebar 3 cm dan tebal 3 cm, dengan waktu perawatan 28 hari.Parameter pengujian yang dilakukan meliputi uji tekan, uji kuat patah, uji kuat pukul densitas dan serapan air. Dari hasil pengujian kuat tekan dan serapan air menunjukkan sampel dengan variasi komposisi terbaik pada campuran 60% dregs, dimana semen dan pasir pada kondisi tetap. Pada komposisi tersebut , sampel yang dihasilkan memiliki karakteristik kuat tekan 8 MPa, densitas 1710 kg/m3, penyerapan air 4,98%, kuat pukul 0,52 MPa dan kuat patah 0,14 MPa.