Pemanfaatan Serbuk Tempurung Kelapa Sebagai Campuran Gipsum Plafon dengan Bahan Pengikat Lateks Akrilik

Abstract

Utilization of research has been conducted as a mixture of sawdust with a binder of gypsum ceiling Acrylix Latex with Hot Press Metod. From the testing that has been done to obtain the physical properties of specimen materials: Density increased in accordance with the addition of sawdust where the maximum density value obtained on the composition 375:25:100, and minimum water uptake value obtained on the composition 375:25:100. This shows the density of the material the better. For optimum mechanical properties obtained on the composition 390:10:100 which impact the value of 1.06 x 10-2 J/cm2 , the value of 1.47 kPa tensile test, the Test 6294.64 kg/cm2 MOE, MOR test value 2.94 MPa. To test DTA, endothermic temperature optimum is obtained on the composition 375:25:100 of 160 0C. While the temperature of gypsum materials endotermiknya 135 0 C.

Telah dilakukan penelitian pemanfaatan serbuk kayu sebagai campuran gipsum plafon dengan bahan pengikat Lateks Acrylix dengan metode hot press. Dari pengujian yang telah dilakukan diperoleh bahwa untuk sifat fisis bahan spesimen: Densitas mengalami kenaikan sesuai dengan penambahan serbuk kayu dimana nilai densitas maksimum diperoleh pada komposisi 375:25:100, dan nilai serapan air minimum diperoleh pada komposisi 375:25:100. Ini menunjukan kepadatan bahan semakin baik. Untuk sifat mekanik nilai optimum diperoleh pada komposisi 390:10:100 dimana nilai impak 1,06 x 10-2 J/cm2 , nilai uji tarik 1,47 kPa, nilai Uji MOE 6294.64 kg/cm2 , nilai uji MOR 2.94 MPa. Untuk uji DTA, suhu endotermik yang optimum diperoleh pada komposisi 375:25:100 yaitu sebesar 160 0 C. Sedangkan bahan gipsum suhu endotermiknya 135 0 C.