Pembuatan dan Karakterisasi Papan Gipsum Plafon yang Dibuat dari Serat Eceng Gondokgipsum- Castable

Abstract

The research has been conducted about preparation and characterization of gypsum board ceiling is made of gypsum powder, castable and eceng gondok fiber. The composition variation of the manufacture of gypsum board ceiling consists of a comparison of the percentage by weight of gypsum powder mixture : castable : eceng gondok fiber are 90:10:0, 89:10:1, 88:10:2, 87:10:3, 86:10:4, 85:10:5, Using a random method with fiber length of 5 cm. From the research, gypsum board ceiling has a value of physical and mechanical properties, density of 1248-1409 kg/m3, water absorption 16.08%, compressive strength 56,068 N/m2, flexural strength 3861,8 N/m2, tensile strength 616,03 N/m2, impact strength 13300 J/m2. Gypsum board ceiling is made can be used up to temperatures of 4100C. Manufacture of gypsum board ceiling by SNI 03-2105- 2006 and JIS 5908-2003

Telah dilakukan penelitian tentang pembuatan dan karakterisasi papan gipsum plafon yang dibuat dari tepung gipsum, tepung castable dan serat eceng gondok. Variasi komposisi pembuatan papan gipsum plafon terdiri dari perbandingan persentase berat campuran tepung gipsum : tepung castable : serat eceng gondok adalah 90:10:0, 89:10:1, 88:10:2, 87:10:3, 86:10:4, 85:10:5, menggunakan metode acak dengan panjang serat 5 cm. Dari hasil penelitian papan gipsum plafon memiliki sifat nilai fisis dan mekanik, densitas 1248-1409 kg/m3, daya serap air 16,08%, kuat tekan 56,068 N/m2, kuat lentur 3861,8 N/m2, kuat tarik 616,03 N/m2, kuat impak 13300 J/m2. Papan gipsum plafon yang dibuat dapat digunakan sampai temperature 4100C. Pembuatan papan gipsum plafon berdasarkan SNI 03- 2105-2006 dan JIS 5908-2003