| dc.description.abstract | Has done research Particle Board Preparation and Characterization of polyester
resin mixed with Corn Fiber Leather. This study aims to determine the addition of
corn husk as a matrix of polyester resin as the fastening of the physical and
mechanical properties of the resulting particle board. From the results of
research based on both physical and mechanical tests showed that charging corn
husk combined with polyester resin with comparisons
30:70,40:60,50:50,60:40,70:30. Polyester Resins: Skin corn can qualify as a
particle board according to the Indonesian National Standard (SNI). Value of
0.63 to 0.94 gr/cm3 density, water content value from 0.221 to 12.403%, thickness
1.01 to 11.42% Value Development, flexural strength value of 91.73 to 340.61
kgf/cm2, strong Imfak 2 , 52 to 3.62 joule/cm2. Strong internal limping from 10.59
to 21.37 kgf/cm2. This sample can be recommended as particle board. | en_US |
| dc.description.abstract | Telah dilakukan penelitian Pembuatan dan Karakterisasi Papan Partikel campuran
resin Poliester dengan Serat Kulit Jagung. Penelitian ini bertujuan untuk
mengetahui penambahan kulit jagung sebagai matriks dalam resin polyester
sebagai pengikatnya terhadap sifat fisis dan mekanik papan partikel yang
dihasilkan. Dari hasil penelitian berdasarkan uji baik fisis maupun mekanik
menunjukkan bahwa pengisian kulit jagung yang digabung dengan resin polyester
dengan perbandingan-perbandingan 30:70,40:60,50:50,60:40,70:30. RP :KJ dapat
memenuhi syarat sebagai papan partikel sesuai dengan Standart Nasional
Indonesia (SNI). Nilai kerapatan 0,63-0,94 gr/cm3, Nilai Kadar air 0,221-
12,403%, Nilai Pengembangan tebal 1,01-11,42%, Nilai kuat lentur 91,73-340,61
kgf/cm2, kuat Imfak 2,52- 3,62 joule/cm2. Kuat rekat internal 10,59 – 21,37
kgf/cm2. Sampel ini dapat direkomendasikan sebagai papan partikel. | en_US |